Cold forging parts

requires much more strength to form the parts according to hot forging parts, small and medium parts are manufacturing with production method of cold forging. Those parts requires to be final product with forming process by automat, knurling, gearing, stress relieving etc. Cold forging parts requires by forming with 6-7 times according to material yield strength. Those parts are manufactured by closed moulding system.

Your technical drawings of cold forging parts are mostly welcome to be supplied.

Header Punches

Hss Raw Material Options:

M2 - M35 - M42

Punches Coating Options:

Tin coated, Ticn coated Tialn coated, Plain.

Size: 12x25, 14x25, 18x25,  23x25 available in our stocks If you offer us your technical drawings custom production is allowed.

Punch Type:

DIN 912, DIN 84, DIN 963, DIN 965,  DIN 7981, DIN 7982,  DIN 7504(Drill Screws), DIN 7985, 6 lobe, Cross recessed raised countersunk head tapping screws, Chipboard Screws, Sheet Metal Screws, Combi Punches, Pozi and Ph Combi Punches, Punch Pins, tapping screws, Countersunk Screws, Panhead Screws, Cheese head screws, Cross recessed countersunk head screws, Torx punches, Micro second punches (#0 recess header punches), ANSI, DIN ve JIS norms are available in our stocks to supply our screw manufacturer partners.

Thread Rolling Dies

are used for forming screw gears, Available rolling dies in our stocks are size of TR0, TR 0.5, TR1, TR2, TR3 with raw material of D2, M2, DC53 and for stainless steel screws we offer M42(Hss) die plates with Black Oxidized thread rolling dies. Those dies are fully performs with Hilgeland, Eww Menn, Sacma, Salvi, Ingramatic, Hartford screw machineries. We offer standart screw rolling dies as Chipboard Screws, Tapping screws, Wood screws, Drywall screws, Hi-Low screws, Ejot gears, Plastic(Pt) Screws, Metric screws and the other screws according to request and for custom screws we offer knurling dies, our dies are properly designed for high speed machineries up to 550-600 pcs screws per minute, specialized dies we offer each customers rapidly.

For more details kindly contact us with your inquiries.

Drilling screws

are manufactured by screw manufacturers those kind of screws are used to drill any sheet material. Drilling screws forms its gear way of any kind of sheet by its own(no required any gear on the sheet) which differs by the other kind of screws. There are many kind of drilling screws so drill point dies are applicable for self drilling screws, Hex Head drilling screws, Pan head drilling screws etc.. Drilling screws are variable as many kind of according to workpiece of sheet metal. Drilling screw mostly used by home appliance manufacturers, lock manufacturers, automotive industry, air condition manufacturers as the for the other industry. Drilling screws must be assembled to sheet metal by drilling speed of 1700-2500 Rpm.

Hss+ Tin coated drill pointing dies: Those kind of dies allows around 500.000-700.000 pieces of drilling screws with low carbon chq wires.

For more details contact us.

Carbide Drill point dies allows production of approximately 2.500.000 pcs of drilling screws on low carbon chq wires.

For more details kindly contact us.

Those kind of carbide tools are used for machining carbide tools and moulds as the same for even high strength steels which approachs hardness of workpiece up to 80-85 Hrc (Rockwell degree). In case of demand we have in stocks with required toolings for lathe manufacturing. Those carbide tools are much more efficient and useful with regular carbide turning inserts.

Carbide Extrusion Pins

are approximately ten times durable comparing with regular high speed steel (M2 or M42) pvd coated extrusion pins workpiece of cold heading machinery. Minimum parts production ranges are 1.5 million on low carbon screw wires which means to keep production much more stable and durable. This kind of carbide extrusion punch pins are also requires in short and middle term minimum setup ranges in manufacturing so production pieces increased compared with regular Hss extrusion pins and causes to minimize labor force.